This item is BWB002A
General Properties | BWB001 | BWB002A | BWB002B | BWB003 |
Al2O3(%) | 92 | 92 | 92 | 92 |
Specific density(g/cm³) | 3.7±0.05 | 3.7±0.05 | 3.7±0.05 | 3.7±0.05 |
Color | White | White | White | White |
Moh's hardness | 9 | 9 | 9 | 9 |
HV(0.5Kg) | 1100±50 | 1100±50 | 1100±50 | 1100±50 |
Crushing strength(MPa) | ≥400 | ≥400 | ≥400 | ≥400 |
Thermal expansion Coeff(×10^-6/ºC) | 7-8 | 7-8 | 7-8 | 7-8 |
Wear Rate(Kg/T) | 0.015 | 0.015 | 0.015 | 0.015 |
Chemical composition | ||||
Al2O3(%) | ≥92 | ≥92 | ≥92 | ≥92 |
SiO2(%) | ≤5 | ≤5 | ≤5 | ≤5 |
Others(%) | ≤3 | ≤3 | ≤3 | ≤3 |
Diameter range(mm) | 0.3-40 | 0.3-40 | 0.3-40 | 0.3-40 |
Application field and equipment | Applicated in nano | Applicated in industries of zirconium silicate, GCC,Kaolin etc. Applicable to ball mills vertical stirring mills etc. | Mainly applicated in zirconium silicate industry, Applicable to ball mills. | Mainly aplicated in ceramic industries, Applicable to ball mills. |
品牌/厂家：百特威尔
型号：BWB001
类型：氧化铝陶瓷
化学成分：超氧化铝
规格：φ0.3-40mm
用途：研磨加工
产地：江西景德镇
莫氏硬度：9
密度：3.7g/cm3
比重：3.7g/cm³
热膨胀系数：7-8*10^-6/℃
吨磨耗：0.020Kg/T*h
颜色：本白
BW Nano ceramic grinding balls is produced by advanced manufacturing process and suitable for all kinds of mills such as stirred mill, roller ball mill and vibratory mill etc. to grind and disperse high efficiently.
BW Nano ceramic grinding balls has the characteristics of high density, high hardness and low wear loss and super-high grinding efficiency.